- Recommended for highly hydrophobic samples
- Available in four
porosities
- Most versatile reverse phase
DAISOGEL
C8-P packing materials are bonded with octyl groups and are fully
endcapped. They are recommended for compounds which are too strongly
retained on C18 phases.
Four pore sizes, namely 6, 12, 20 and 30nm are available
to optimise the separation depending on the solutes‘ molecular
size. 20 and 30nm materials are widely used for larger molecules
with higher hydrophobicity. |
| Product names and properties / analytical grades (minimum lot: 50g) |
| |
Pore Size (nm) |
Particle Size (um) |
Pore Volume (mL/g) |
Surface Area (m2/g) |
% of Carbon |
| SP-60-3-C8-P |
6 |
3 |
0.75 |
450 |
14 |
| SP-60-5-C8-P |
6 |
5 |
0.75 |
450 |
14 |
| SP-120-3-C8-P |
12 |
3 |
1 |
300 |
10 |
| SP-120-5-C8-P |
12 |
5 |
1 |
300 |
10 |
| SP-200-3-C8-P |
20 |
3 |
1.1 |
200 |
7 |
| SP-200-5-C8-P |
20 |
5 |
1.1 |
200 |
7 |
| SP-300-3-C8-P |
30 |
3 |
0.9 |
100 |
4 |
| SP-300-5-C8-P |
30 |
5 |
0.9 |
100 |
4 |
|
| Product names and properties / preparative grades (minimum lot: 500g) |
| |
Pore Size (nm) |
Particle Size (um) |
Pore Volume (mL/g) |
Surface Area (m2/g) |
% of Carbon |
| SP-60-10-C8-P |
6 |
10 |
0.75 |
450 |
14 |
| SP-60-15-C8-P |
6 |
15 |
0.75 |
450 |
14 |
| SP-60-20-C8-P |
6 |
20 |
0.75 |
450 |
14 |
| SP-60-40/60-C8 |
6 |
50 |
0.75 |
450 |
14 |
| SP-120-10-C8-P |
12 |
10 |
1 |
300 |
10 |
| SP-120-15-C8-P |
12 |
15 |
1 |
300 |
10 |
| SP-120-20-C8-P |
12 |
20 |
1 |
300 |
10 |
| SP-120-40/60-C8 |
12 |
50 |
1 |
300 |
10 |
| SP-200-10-C8-P |
20 |
10 |
1.1 |
200 |
7 |
| SP-200-15-C8-P |
20 |
15 |
1.1 |
200 |
7 |
| SP-200-20-C8-P |
20 |
20 |
1.1 |
200 |
7 |
| SP-200-40/60-C8 |
20 |
50 |
1.1 |
200 |
7 |
| SP-300-10-C8-P |
30 |
10 |
0.9 |
100 |
4 |
| SP-300-15-C8-P |
30 |
15 |
0.9 |
100 |
4 |
| SP-300-20-C8-P |
30 |
20 |
0.9 |
100 |
4 |
| SP-300-40/60-C8 |
30 |
50 |
0.9 |
100 |
4 |
|